Yazar "Tepehan, Fatma Zehra" seçeneğine göre listele
Listeleniyor 1 - 5 / 5
Sayfa Başına Sonuç
Sıralama seçenekleri
Yayın Ceramic encapsulated latex composites(Elsevier Inc, 2006-04-15) Uğur, Şaziye; Pehlivan, Esat; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderThis work reports the encapsulation of latex particles in Al(2)O(3)-polystyrene (PS) composite films. These films were prepared from PS particles in Al(2)O(3) dispersion at room temperature in various latex contents. Composite films were annealed at elevated temperatures in 10 min time interval above the glass transition temperature (T,,) of polystyrene. Transmitted photon intensities. I(tr) were monitored after each annealing step. AFM micrographs were also used to observe the physical changes of the composite films during annealing. It was observed that latex particles are encapsulated above a critical Al(2)O(3) content of 33 wt% which corresponds to the critical occupation probability of p(c) = 0.33 at which the film obey the site-percolation model with a critical exponent of 0.45. Below pc it was seen that complete latex film formation process took place, where transparency of the film was increased by annealing.Yayın Dissolution of Al2O3-polystyrene latex composites: A fluorescence study(Taylor & Francis Ltd, 2005) Uǧur, Şaziye; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderThis work reports the use of the steady state fluorescence (SSF) technique to study dissolution of a composite film formed from a mixture of Al 2O3 and polystyrene (PS) latex particles. The composite films were cast from dispersion of pyrene (P)-labeled PS particles in Al 2 O3 solution at room temperature and annealed at 280°C temperature for 10 min. Eight different composite films were studied in various latex contents. Toluene was used as dissolution agent. Fluorescence intensities Ip from P were monitored during dissolution. Fickian diffusion was employed to model the dissolution processes. Dissolution coefficients, D d, were measured and found to be increased at high PS content in the composite films.Yayın Film formation from nano-sized polystrene latex covered with various TiO2 layers(Wiley, 2006-12) Uğur, Şaziye; Sunay, Selin; Elaissari, Abdelhamid; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderSteady-state fluorescence technique was used for studying film formation from TiO2 covered nano-sized polystyrene latex particles. The composite films were prepared from pyrene (P)-labeled PS particles by covering them with various layers of TiO2 at room temperature. These films then annealed at elevated temperatures in 10 min time interval above glass transition (T-g) temperature of polystyrene. Five different composite films were studied in various TiO2 layer contents. Fluorescence emission intensity, I-P from P was measured after each annealing step to monitor the stages of film formation. Films present significant increase in I-P above the certain onset temperature called minimum film forming temperature, To. However, at higher annealing temperatures, I-P showed a decrease. Increase and decrease in I-P were modeled by void closure and interdiffusion processes and related activation energies were determined, respectively. Dissolution of annealed PS film, with high TiO2 content presented a nice, ordered nanosized ceramic structure, which may predict the construction of nano-layer photonic crystals.Yayın Film formation from TiO2-polystyrene latex composite: a fluorescence study(Taylor & Francis Group, 2007-03-01) Uğur, Şaziye; Sunay Yapışkan, Münüre Selin; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderThis work reports the use of the steady state fluorescence (SSF) technique for studying film formation from TiO2 covered polystyrene (PS) latex particles. The composite films were prepared from pyrene (P)-labeled PS particles by covering them with TiO2 at room temperature and then annealed at elevated temperatures in 10 min time interval above glass transition (T-g) temperature of polystyrene. Five different composite films were studied in various TiO2 layer contents. Fluorescence intensities Ip from P were measured after each annealing step to monitor the stages of film formation. Films showed considerable increase in Ip above the certain onset temperature called minimum film forming temperature, T-0. Void closure and interdiffusion stages were modeled and related activation energies were determined and found to be 23.12 and 92.80 kJ mol(-1), respectively.Yayın Fluorescence study on Al2O3-polystyrene latex composite film formation(John Wiley & Sons Inc, 2005-06) Uğur, Şaziye; Salman, Oğuz Umut; Tepehan, Galip Gültekin; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderThis work reports a steady state fluorescence (SSF) technique for studying film formation from mixture of Al2O3 and polystyrene (PS) latex particles. The composite films were prepared from dispersion of pyrene (P)labeled PS particles in Al2O3 solution at room temperature and annealed at elevated temperatures in 10-min time interval above glass transition (T-g) temperature of polystyrene. Nine different composites film were studied in various latex contents. Fluorescence intensities (I-P) from P were measured after each annealing step to monitor the stages of film formation. No variations in I-p were detected for the films prepared with higher than 33 wt% Al2O3 content. However films prepared below 33 wt% Al2O3 content show considerable increase in I-P above the certain onset temperature called minimum film forming temperature, To. Healing temperatures T., were determined from the maxima of I-P. Void closure and interdiffusion stages were modeled and related activation energies were determined and found to be 20 and 97 kJ.mol(-1), respectively.