    Tribo-corrosion behavior of electroplating, nitrocarburizing, and QPQ processes on barrel finishing
    (Walter de Gruyter GmbH, 2023-11-27) Yücel, Aysu Hande; Yılmaz, Alpay; Bakkal, Mustafa; Kuzu, Ali Taner
    In this study, the effects of nitrocarburizing, QPQ, and Cr coating on the surface properties of 32CrMoV12-10 gun barrels are discussed. Hardness measurements, pin-on-disc tests, and anodic polarization tests were performed to examine the hardness values, wear resistance, friction coefficient, and corrosion resistance. The hardness of the specimen treated with QPQ was found to be the highest. Comparing the hardness profiles, it was observed that the casing depth of the nitrocarburized sample was shallower than that of the QPQ-treated sample. The pin-on-disc test revealed that the nitrocarburized sample exhibited a high coefficient of friction, while the Cr-coated sample showed the lowest coefficient of friction. Analyzing the Tafel polarization curve, it was determined that the nitrocarburized and QPQ-treated specimens demonstrated similar levels of corrosion resistance. However, it can be noted that the QPQ-treated specimen had a slightly lower corrosion rate.
  • Küçük Resim
    Yayın
    Analysis of mechanical behavior of termoplastic composites
    (Necip Fazıl YILMAZ, 2022-03-04) Kuzu, Ali Taner; Kosemen, Elifnur; Yücel, Aysu Hande; Bakkal, Mustafa
    This paper presents the effect of fiber orientation on the tensile, compression, impact, and flexuralproperties of glass fiber reinforced acrylic-based thermoplastic composites. The mechanical behaviorof three different composite plates, produced by the resin transfer molding (RTM) method, with0°/90°/45°, 0°/90° and ±45° glass fiber orientations were investigated by carrying out tensile,compression, three-point bending and Charpy impact tests. A Weibull distribution model wasimplemented to explain the variation in mechanical properties of the acrylic-based composite.According to Weibull analysis results with 63.2% probability, the highest tensile strength (561 MPa),compressive strength (293 MPa) and impact values (19.44 J) were obtained when the plate with0°/90° glass fiber orientation was tested, whereas the highest flexural strength was obtained when theplate with 0°/90°/45° was tested.