11 sonuçlar
Arama Sonuçları
Listeleniyor 1 - 10 / 11
Yayın Time evolution of film formation from polystyrene particles: a percolation approach(Springer, 2005-12) Uğur, Şaziye; Pekcan, Mehmet ÖnderThis work reports the film formation process from surfactant-free polystyrene (PS) latex particles. Steady state fluorescence and photon transmission techniques were used to study the evolution of film formation. The films were prepared from fluorescein (F)-labeled PS latex particles at room temperature and annealed in 2.5-min-time intervals above the glass transition temperature (T-g) of PS. Fluorescence intensity (I-F) from F was measured after each annealing step to monitor the stages of film formation. Evolution of transparency of latex films was monitored by using the photon transmission intensity, I-tr. Drastic increase in I-tr and I-F above the critical annealing times t(r) and t(c) respectively, were attributed to the percolation behavior of the PS material. Critical exponents, beta, of percolation clusters were measured and found to be around 0.31 and 0.37 for Itr and IF measurement, respectively, which were attributed to the site percolation model.Yayın Swelling of iota-carrageenan gels prepared with various CaCl2 content: A fluorescence study(European Polymer Federation, 2008-01-05) Tarı İlgin, Özlem; Pekcan, Mehmet ÖnderIota carrageenan gels prepared with various CaCl2 content were completely dried and then swelled in water vapor. Steady-state fluorescence ( SSF) technique was used to monitor the swelling process of each iota carrageenan gels at various temperatures. Pyranine was used as a fluorescence probe. Apparent fluorescence intensity, I increased as swelling time increased for all gel samples. The increase in I was modelled using Li-Tanaka equation from which the swelling time constants, tau(1) and cooperative diffusion coefficients, D-c were determined. It was observed that D-c increased as the swelling temperature was increased. On the other hand at each temperature, it was seen that D-c decreased as CaCl2 content was increased. Activation energies for swelling were obtained and found to be 60.5, 61.0, 61.5 and 62.8 kJmol(-1) for the gels prepared with increasing amount of CaCl2 content.Yayın Film formation from TiO2-polystyrene latex composite: a fluorescence study(Taylor & Francis Group, 2007-03-01) Uğur, Şaziye; Sunay Yapışkan, Münüre Selin; Tepehan, Fatma Zehra; Pekcan, Mehmet ÖnderThis work reports the use of the steady state fluorescence (SSF) technique for studying film formation from TiO2 covered polystyrene (PS) latex particles. The composite films were prepared from pyrene (P)-labeled PS particles by covering them with TiO2 at room temperature and then annealed at elevated temperatures in 10 min time interval above glass transition (T-g) temperature of polystyrene. Five different composite films were studied in various TiO2 layer contents. Fluorescence intensities Ip from P were measured after each annealing step to monitor the stages of film formation. Films showed considerable increase in Ip above the certain onset temperature called minimum film forming temperature, T-0. Void closure and interdiffusion stages were modeled and related activation energies were determined and found to be 23.12 and 92.80 kJ mol(-1), respectively.Yayın Small molecule diffusion into swelling Iota-Carrageenan gels: A fluorescence study(Taylor & Francis Group, 2007-04) Ataman, Evren; Pekcan, Mehmet ÖnderSmall molecule diffusion into Iota-Carrageenan gel was studied by using steady-state fluorescence (SSF) technique. Pyranine, dissolved in water was used as fluorescence probe. Fluorescence emission intensity, I-p, and scattered light intensity, I-sc, were monitored to study diffusion and swelling processes at various temperatures respectively. Fickian and Li-Tanaka models were elaborated to produce diffusion, D, and collective diffusion, D-0, coefficients. Diffusion and swelling activation energies were also obtained and found to be 20.5 kj mol(-1) and 28.2 kj mol(-1). respectively.Yayın Films formed from polystyrene latex/clay composites: A fluorescence study(Springer New York, 2005-07) Uğur, Şaziye; Alemdar, Ayşe; Pekcan, Mehmet ÖnderThis study reports a steady-state fluorescence (SSF) technique for studying film formation from surractant-free polystyrene (PS) latex and Na-montmorillonite (SNaM) composites. The composite films were prepared from pyrene (P)-labeled PS particles and SNaM clay at room temperature and annealed at elevated temperatures in 10-min intervals above glass transition temperature (T-g) of polystyrene. During the annealing processes, the transparency of the fllm improved considerably. Scattered light (I-s) and fluorescence intensity (I-s) from P were measured after each annealing step to monitor the stages of film formation. Evolution of transparency of composite films was monitored by using photon transmission intensity, I-tr Scanning electron microscopy (SEM) was used to detect the variation in physical structure of annealed composite-films. Minimum flIm formation temperature, T-o, and healing temperatures, T-h, were determined. Void closure and interdiff-usion stages were modeled and related activation energies were determined. It was observed that both activation energies increased as the percent of SNaM was increased in composite films.Yayın Phase transitions of kappa-carrageenan gels in various types of salts(John Wiley & Sons Inc, 2006-11-05) Kara, Selim; Arda, Ertan; Kavzak, Burhan; Pekcan, Mehmet ÖnderSol-gel and gel-sol phase transitions of K-carrageenan in various types of salts were studied using photon transmission technique. Here, LiCl, NaCl, KCl, MgCl2, CaCl2, and SrCl2 were chosen as the proper salts for the K-carrageenan-water system. Photon transmission intensity, I-tr was monitored against temperature to determine the sol-gel and gel-sol temperatures (T-sg and T-gs) and activation energies (Delta E-sg and Delta E-gs). It was observed that T-gs temperatures were notably higher than T-sg due to the hysteresis on the phase transition loops. It was observed that stronger carrageenan gels are formed in the presence of KCl compared to the others.Yayın Film formation from nano-sized polystyrene latex particles(John Wiley & Sons Ltd, 2005-05) Uğur, Şaziye; Elaissari, Abdelhamid; Pekcan, Mehmet ÖnderThis work reports on the steady state fluorescence (SSF) technique for studying film formation from surfactant-free, nano-sized polystyrene (PS) latex particles prepared via emulsion polymerization. The latex films were prepared from pyrene M-labeled PS particles at room temperature and annealed at elevated temperatures in 5, 10, 15, 20 and 30 min time intervals above the glass transition temperature (T-g) of PS. During the annealing processes, the transparency of the film was improved considerably. Monomer and excimer fluorescence intensities, I-p and I-E respectively, from P were measured after each annealing step to monitor the stages of film formation. Evolution of transparency of the latex films was monitored by using photon transmission intensity, It,. Void closure and interdiffusion stages were modeled and related activation energies were determined and found to be 10.3 and 50.3 kJ mol(-1). Void closure temperatures, T-v, were determined from the minima of I-tr value. CopyrightYayın Film formation from PS latex doped PNIPAM hydrogels at various heating and cooling rates(VSP BV, Brill Academic Publishers, 2008-05-01) Uğur, Şaziye; Yargı, Önder; Pekcan, Mehmet ÖnderFilm formation from polystrene (PS) latex doped poly(N-isopropylacrylamide) (PNIPAM) hydrogels was studied by using photon transmission technique. The transmitted light intensity, It, was monitored during film formation process. Films were prepared by annealing, 10 wt% PS doped PNIPAM particles at five different heating and cooling rates at temperatures ranging from 10 to 100 degrees C. I-tr presented a hysteresis loops during heating-cooling cycles, which were explained by void closure and void reconstruction processes. The corresponding activation energies were measured during reversible film formation process. Void closure and void reconstruction models were introduced to produce the activation energies.Yayın Film formation stages for poly(vinyl acetate) latex particles: a photon transmission study(Springer-Verlag, 2006-07) Kara, Selim; Pekcan, Mehmet Önder; Saraç, Ayfer; Arda, ErtanPhoton transmission technique was used to monitor the evolution of transparency during film formation from poly(vinyl acetate) (PVAc) latex particles. The latex films were prepared below the glass transition temperature (T-g) of PVAc. These films were annealed at elevated temperatures in various time intervals above the T-g of PVAc. It is observed that transmitted photon intensity (I-tr) from these films increased as the annealing temperature is increased. It is seen from I (tr) curves that there are two film formation stages. These successive stages are named void closure (viscous flow) and interdiffusion. The activation energies for viscous flow (Delta H) and backbone motion (Delta E (b)) were obtained by using well-defined models. The averaged values of the backbone (Delta E (b)) and the viscous flow activation energies (Delta H) were found to be 188.6 and 5.6 kcal/mol, respectively. The minimum film formation (tau (M),T (M)) and healing points (tau (H),T (H)) were determined. Minimum film formation (Delta E (M)) and healing activation energies (Delta E (H)) were measured using these time-temperature pairs. Delta E (M) and Delta E (H) were found to be 32.5 and 28.3 kcal/mol, respectively.Yayın Reversible film formation from nano-sized PNIPAM particles below glass transition(Springer-Verlag, 2007-01) Uğur, Şaziye; Elaissari, Abdelhamid; Yargı, Önder; Pekcan, Mehmet ÖnderReversible film formation process from nano-sized Poly(N-isopropylacrylamide) (PNIPAM) microgel particles were studied during heating-cooling cycles at various rates. Photon transmission technique was used and transmitted photon intensity I (tr) was monitored during heating-cooling cycles. The increase and decrease in I (tr) during heating and cooling was explained with the void closure and void reconstruction processes, and the corresponding activation energies were measured. It was observed that PNIPAM microgels required less energy during reconstruction of voids than their closure.